Precautions for use

• Since heat resistance and chemical resistance changes according to use conditions, ensure to test under actual use conditions beforehand.

• Exposure to water or vapor at high temperatures may significantly reduce the mechanical strength due to hydrolysis. Therefore, avoid exposure to water or vapor at high temperatures.

• Avoid exposure to ammonia as it accelerates hydrolysis.

• Exposure to organic solvents or oils may cause cracks even at low stress. Moreover, cracks may be caused by plasticizing agents contained in rubber and PVC (Polyvinyl Chloride). Therefore, avoid exposure to organic solvents, oils, rubber and PVC.

• Black spots (sludge) may appear on the external surface. However, this has no impact on performance.

• Discoloration to some extent may occur depending on lot and various conditions.

• Size available in stock, configuration and manufacturers of raw materials used may change without any notice.

• Since heat resistance and chemical resistance changes according to use conditions, ensure to test under actual use conditions beforehand.

• As it is not resistant to strong acids and strong basis, especially since resistance to strong acids is very weak, avoid applications that need exposure to them.

• Since copper is a decomposition catalyst, avoid applications that need exposure to copper at the time of melting (insert of brass etc.)

• As resistance weather is low, precaution is necessary in case of outdoor use.

• As it is inflammable, it is necessary to keep it away from heat and fire sources during handling and storage.

• Black spots (sludge) may appear on the external surface. However, this has no impact on performance.

• Discoloration to some extent may occur depending on lot and various conditions.

• Size available in stock, configuration and manufacturers of raw materials used may change without any notice.

• Since heat resistance and chemical resistance changes according to use conditions, ensure to test under actual use conditions beforehand.

• Black spots (sludge) may appear on the external surface. However, this has no impact on performance.

• Discoloration to some extent may occur depending on lot and various conditions.

• Size available in stock, configuration and manufacturers of raw materials used may change without any notice.